Optically anisotropic compound and resin composition comprising the same

ABSTRACT

Disclosed is a silicon containing compound represented by Formula 1 which has high optical anisotropy and high compatibility with a polymer resin. Also, a resin composition including the compound and a polymer resin, and an optical member including the resin composition are disclosed. Since the silicon containing compound represented by Formula 1 has high compatibility with a polymer resin and high optical anisotropy, in the case of an optical member obtained by using a polymer resin composition including the silicon containing compound, there is no phase separation, and it is possible to achieve a required optical characteristic with only a small amount thereof.

TECHNICAL FIELD

The present invention relates to a silicon containing compound having high compatibility with a polymer resin and high optical anisotropy. Also, the present invention relates to a resin composition including the compound, and an optical member including the resin composition.

BACKGROUND ART

Recently, with the development of the electronics industry, the use of a polymer resin for optical use has rapidly increased. For example, the demand for various polymer materials for optical use, such as an optical disc substrate used as a storage medium, an optical lens, an optical fiber used for optical communication, a fresnel lens for a projection screen, a prism sheet used in a liquid crystal display, a protective film for a polarizing plate, a compensation film, etc., has been rapidly increased.

Such polymer resins for optical use are usually required to be optically isotropic, but a polymer resin of a final product may be anisotropic due to its own structure or stress during the process. Also, an optical resin, when inserted in a multi-layered structure, may have optical anisotropy by thermal expansion/contraction between respective layers.

When a film, lens, etc. with such optical anisotropy exists in an optical path, a property of the phase may be changed, thereby adversely affecting signal reading. Therefore, it is preferable to use an optical member including an optical resin of which anisotropy is reduced as much as possible.

On the other hand, optical birefringence may be artificially given. For example, in the case of a liquid crystal display, the contrast at an inclined viewing angle may be degraded due to optical birefringence caused by the liquid crystal and a polarizing film. In order to solve this problem, a polymer resin having optical anisotropy with a certain direction may be used to compensate the birefringence caused by the liquid crystal and the polarizing film, thereby improving a viewing angle. In the case of a polymer resin for optical use as mentioned above, the optical characteristic is required to be controlled in a required direction.

As a conventional technology of controlling the optical characteristic of a polymer, a birefringence control method through adjustment of the structure of a polymer resin, such as Japanese Laid-Open Patent Nos. 1990-129211 and 2000-044614, has been known. However, the method has a problem in that the composition of a monomer of a copolymer is required to be changed to control the birefringence, and the change in the composition of the monomer may change other physical properties of the polymer resin.

Also, as a birefringence control method of a polymer resin, methods of adding an anisotropic material have been known. Japanese Laid-Open Patent No. 2004-035347 disclosed a method of introducing a needle-shaped inorganic particle as an anisotropic material to adjust an optical characteristic. However, in the case of an inorganic fine particle, it is difficult to uniformly disperse the particle in a solvent due to low solubility in the solvent, and high density, and there is a possibility that the particle is subject to aggregation due to low stability, thereby reducing the transparency of the polymer resin. Also, Japanese Laid-Open Patent No. Hei 8-110402 disclosed a method of adjusting the optical characteristic of a polymer resin by adding a low-molecular organic compound. In general, compounds with high anisotropy have disadvantages, such as high crystallinity, low solubility in a solvent, and low compatibility with the polymer resin. Thus, the compounds, when mixed, may be precipitated by crystallization, and may be not dissolved in a solvent. However, there is no specific solution for such problems.

DISCLOSURE Technical Problem

Therefore, the present invention has been made in view of the above-mentioned problems. The present invention provides an optically anisotropic compound which has high optical anisotropy and high solubility in a solvent, can effectively control the optical characteristic of a polymer resin with only a small amount thereof, and does not cause a problem, such as precipitation, due to high compatibility with the polymer resin.

Also, the present invention provides a resin composition including the optically anisotropic material and the polymer resin.

Technical Solution

In accordance with an aspect of the present invention, there is provided a silicon containing compound represented by Formula 1:

In Formula 1,

represents

each of Q¹ to Q¹² independently represents —H, —F, —Cl, —Br, —I, —CN, —CF₃, —OCF₃, —OR⁶, —NHR⁶, —NR⁶R⁶ or —C(═O)R⁶;

Z represents C or N, and herein, if Z is N, there is no bond with corresponding Q¹ to Q¹²;

each of l, m and n independently represents an integer of 0 to 2, and l+m+n represents an integer equal to or greater than 1;

each of Y, G¹ and G² independently represents —(CH₂)_(r)SiW¹W²(CH₂)_(s)—, —O—, —NR⁶—, —S—, —SO—, —SO₂—, —(CH₂)_(q)—, —CH═CH—, —C≡C—, —C(═O)O(CH₂)_(q)—, —OC(═O)(CH₂)_(q)—, —(CH₂)_(q)C(═O)O—, —(CH₂)_(q)OC(═O)—, —C(═O)(CH₂)_(q)—, —(CH₂)_(q)C(═O)—, —C(═O)NR⁶—, NR⁶C(═O)—, —C(═O)S—, or —SC(═O)—, q represents an integer of 0 to 5, each of r and s independently represents an integer of 0 to 2;

E represents —H, —F, —Cl, —Br, —I, —CN, —NCO, —NCS, —SiW¹W²R⁶, —R⁶, —N(R⁶)₂, —OR⁶, —CF₃, or —OCF₃;

each of X¹ to X⁵ independently represents —SiW¹W²—, —O—, —NR⁶—, —S—, —SO—, —SO₂—, —(CH₂)_(p)—, —C(═O)NR⁶—, —NR⁶C(═O)—, —NR⁶C(═O)NR⁶—, —C(═O)O—, —OC(═O)—, or —OC(═O)O—, and p represents an integer of 0 to 2;

W¹ represents —R⁷, —OR⁷, —NHR⁷, or —N(R⁷)₂;

W² represents —R⁸, —OR⁸, —NHR⁸, or —N(R⁸)₂;

each of R¹ to R⁸ independently represents —H, C₁˜C₂₀ alkyl, C₁˜C₂₀ fluoroalkyl, C₂˜C₂₀ alkenyl, C₂˜C₂₀ fluoroalkenyl, C₂˜C₂₀ alkynyl, C₂˜-C₂₀ fluoroalkynyl, —(CH₂CH₂O)_(t)CH₃, —(CH₂CHCH₃O)_(t)CH₃, or —(CHCH₃CH₂O)_(t)CH₃, and t represents an integer of 1 to 5; and

at least one of Y, G¹, G², E, and X¹ to X⁵ is a Si containing substituent, and herein, as the Si containing substituent, in Y, G¹ and G², —(CH₂)_(r)SiW¹W²(CH₂)_(s)— is introduced, in E, —SiW¹W²R⁶ is introduced, and in X¹ to X⁵, —SiW¹W²— is introduced.

In accordance with another aspect of the present invention, there is provided a resin composition including a polymer resin and the silicon containing compound represented by Formula 1.

In accordance with a further aspect of the present invention, there is provided an optical member including the resin composition.

ADVANTAGEOUS EFFECTS

A silicon containing compound represented by Formula 1 of the present invention has high compatibility with a polymer resin and high optical anisotropy. Accordingly, in the case of an optical member obtained by using a polymer resin composition including the silicon containing compound represented by Formula 1, there is no phase separation, and it is possible to achieve a required optical characteristic with only a small amount thereof.

DESCRIPTION OF DRAWINGS

FIGS. 1 and 2 are optical microscopic photographs (×5) showing the results of the compatibility tests according to Examples 3 and 4; and

FIGS. 3 and 4 are optical microscopic photographs (×5) showing the results of the compatibility tests according to Comparative Examples 1 and 2.

BEST MODE

Hereinafter, the present invention will be described in detail.

The compound represented by Formula 1 of the present invention is an optically anisotropic compound having refractive anisotropy of 0.2 or more, and necessarily has at least one silicon group. In Formula 1, at least one of Y, G¹, G², E, and X¹ to X⁵ is a Si containing substituent. Specifically, as the Si containing substituent, in Y, G¹ and G², —(CH₂)_(r)SiW¹W² (CH₂)_(S)— is introduced, in E, —SiW¹W²R⁶ is introduced, and in X¹ to X⁵, —SiW¹W²— is introduced.

In Formula 1 of the present invention, examples of C₁˜C₂₀ alkyl of R¹ to R⁸ include linear or branched alkyls, such as —CH₃, —CH₂CH₃, —CH₂CH₂CH₃, —CH(CH₃)₂, —CH₂CH₂CH₂CH₃, —CH(CH₃)CH₂CH₃, —CH₂CH(CH₃)₂, etc., but the present invention is not limited thereto. Also, in Formula 1, C₁˜C₂₀ fluoroalkyl of R¹ to R⁸ includes at least one fluorine group substituting for hydrogen of the alkyl group as defined above.

Also, in Formula 1, examples of C₂˜C₂₀ alkenyl of R¹ to R⁸ include linear or branched alkenyls, such as —CH═CH₂, —CH═CHCH₃, —CCH₃═CH₂, —CH₂CH═CH₂, —CH═CHCH₂CH₃, —CH═C(CH₃)₂, —CCH₃═CHCH₃, —CH₂CH═CHCH₃—CH₂CCH₃═CH₂—CHCH₃CH═CH₂ CH₂CH₂CH═CH₂, etc., but the present invention is not limited thereto. Also, in Formula 1, C₂˜C₂₀ fluoroalkenyl of R¹ to R⁸ includes at least one fluorine group substituting for hydrogen of the alkenyl group as defined above.

Also, in Formula 1, examples of C₂˜C₂₀ of R¹ to R⁸ include linear or branched alkynyls, such as —C≡CH, —CH₂C≡CH, —C≡CCH₃, —CH₂CH₂C≡CH, —CHCH₃C≡CH, —CH₂C≡CCH₃, —C≡CCH₂CH₃, etc., but the present invention is not limited thereto. Also, in Formula 1, C₂˜C₂₀ fluoroalkynyl of R¹ to R⁸ includes at least one fluorine group substituting for hydrogen of the alkynyl group as defined above.

Also, in Formula 1, l+m+n represents an integer equal to or greater than 1, preferably an integer of 1 to 4, and more preferably an integer of 1 to 3.

The compound represented by Formula 1 of the present invention is easily mixed with various polymer resins, and has high solubility, even at low temperatures. In addition, the compound is physically and chemically stable under the condition where a liquid crystal display device is usually used, and is stable under heat and light.

Therefore, the compound represented by Formula 1 may be mixed with various polymer resins to control the optical characteristic of a polymer resin.

Specific examples of the compound represented by Formula 1 are as follows, but the present invention is not limited thereto.

Hereinafter, the method of preparing the compound represented by Formula 1 will be described. However, the Reaction Schemes are illustrative only and do not limit the method.

The compound represented by Formula 1 may be prepared by Reaction Scheme 1.

In Reaction Scheme 1, ring A, ring B, ring C, ring D, l, m, n, G¹, G², and E are the same as defined in Formula 1, and each of L¹ and L² independently represents a living group, such as halide, mesylate, tosylate, or triflate.

In Reaction Scheme 1, acetylenes such as trimethylsilylacetylene and Pd catalyst may be used to prepare the tolane compound.

Also, the compound represented by Formula 1 may be prepared by Reaction Scheme 2.

In Reaction Scheme 2, ring A, ring B, ring C, ring D, l, m, n, W¹, W², r, s, G¹, G² and E are the same as defined in Formula 1, each of L¹ and L² is the same as defined in Reaction Scheme 1, and Li or Mg represents a metal capable of forming anions, such as Li, n-BuLi, Mg, etc.

Also, the compound represented by Formula 1 may be prepared by Reaction Scheme 3.

In Reaction Scheme 3, ring A, ring B, ring C, ring D, l, m, n, G¹, G², R⁶ and E are the same as defined in Formula 1, and L¹ is the same as defined in Reaction Scheme 1.

Also, the compound represented by Formula 1 may be prepared by Reaction Scheme 4.

In Reaction Scheme 4, ring A, ring B, ring C, ring D, l, m, n, G¹, G² and E are the same as defined in Formula 1.

In Reaction Schemes 3 and 4, an aryl substitution reaction may be used to synthesize a compound in which Y=NR⁶, O, S, etc., and an oxidation reaction may be used to introduce SO and SO₂.

Also, the compound represented by Formula 1 may be prepared by Reaction Scheme 5.

In Reaction Scheme 5, ring A, ring B, ring C, ring D, l, m, n, q, G¹, G² and E are the same as defined in Formula 1, each of L¹ and L² is the same as defined in Reaction Scheme 1, and Li or Mg represents a metal capable of forming anions, such as Li, n-BuLi, Mg, etc.

As described in Reaction Scheme 5, through a nucleophilic substitution reaction, a compound in which Y═(CH₂)_(q), CH═CH, CO may be prepared.

Also, the compound represented by Formula 1 may be prepared by Reaction Scheme 6.

In Reaction Scheme 6, ring A, ring B, ring C, ring D, l, m, n, q, G¹, G², R⁶ and E are the same as defined in Formula 1, L¹ is the same as defined in Reaction Scheme 1, and Li or Mg represents a metal capable of forming anions, such as Li, n-BuLi, Mg, etc.

Also, the compound represented by Formula 1 may be prepared by Reaction Scheme 7.

In Reaction Scheme 7, ring A, ring B, ring C, ring D, l, m, n, q, G¹, G², R⁶ and E are the same as defined in Formula 1, L¹ is the same as defined in Reaction Scheme 1, Li or Mg represents a metal capable of forming anions, such as Li, n-BuLi, Mg, etc., and P represents a protection group.

Based on Reaction Schemes 6 and 7, a CO₂H group may be prepared by bubbling CO₂ gas, and an OH group may be introduced by using (Me₃SiO)₂. Herein, SOCl₂, COCl₂, MsCl, TsCl, EDC, DCC, etc. may be used to prepare an ester compound, or Dean-Stark may be used to carry out an esterification reaction.

In the method of preparing the compound represented by Formula 1 according to the present invention, any reactant capable of showing the same or similar effects to that of the reactant used in Reaction Schemes 1 to 7 may be used, and any preparation method having a similar scheme to that of Reaction Schemes 1 to 7 may be employed.

A resin composition according to the present invention includes a polymer resin and a silicon containing compound represented by Formula 1 of the present invention. Herein, the silicon containing compound represented by Formula 1 may play a role of controlling the optical characteristic of the polymer resin.

When used for such a purpose, the silicon containing compound represented by Formula 1 may be used alone or in combination. Also, within the resin composition, the polymer resin and the anisotropic compound represented by Formula 1 may be used in a weight ratio of 50:50 to 99:1, preferably of 70:30 to 99:1, and more preferably of 80:20 to 99:1.

As the polymer resin, which can be mixed with the compound represented by Formula 1, a conventional polymer resin for optical use may be used with no particular limitation. Examples of the polymer resin include polyimide, polyamide imide, polyamide, polyetherimide, polyetheretherketone, polyetherketone, polyketone sulfide, polyethersulfone, cycloolefin polymer, polysulfone, polyphenylene sulfide, polyphenylene oxide, polyethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate, polyacetal, polycarbonate, polyacrylate, acrylic resin, polyvinyl alcohol, polypropylene, cellulose, triacetyl cellulose, epoxy resin, phenol resin, etc., but the present invention is not limited thereto. Also, the polymer resins may be used alone or in combination, and herein, the use amount is not particularly limited.

Also, the resin composition according to the present invention may include an organic solvent as required, in addition to the polymer resin, and the anisotropic compound. The organic solvent included in the composition facilitates the application (coating) of the resin composition of the present invention on a substrate.

Herein, as the organic solvent, conventional organic solvents known in the art may be used without any particular limitation. Non-limiting examples of the organic solvent include: hydrocarbons such as cyclohexane, cyclopentane, benzene, toluene, xylene, butylbenzene, etc.; ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, etc.; esters such as ethyl acetate, ethylene glycol monomethyl ether acetate, propylene glycol monomethyl ether acetate, gamma-butyrolactone, etc.; amides such as 2-pyrrolidone, N-methyl-2-pyrrolidone, dimethylformamide, dimethylacetamide, etc.; halogens such as chloroform, dichloromethane, carbon tetrachloride, dichloroethane, tetrachloroethane, tetrachloroethylene, chlorobenzene, etc.; alcohols such as t-butyl alcohol, diacetone alcohol, glycerin, monoacetin, ethylene glycol, triethylene glycol, hexylene glycol, ethylene glycol monomethyl ether, etc.; phenols such as phenol, parachlorophenol, etc.; and ethers such as methoxybenzene, 1,2-dimethoxybenzene, diethylene glycol dimethyl ether, ethylene glycol dimethyl ether, ethylene glycol diethyl ether, propylene glycol dimethyl ether, propylene glycol diethyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, dipropylene glycol dimethyl ether, dipropylene glycol diethyl ether, etc. Also, the organic solvents may be used alone or in combination, and herein, the use amount is not particularly limited.

Also, the resin composition of the present invention may include a surfactant as required. A surfactant may be used to allow the composition to be easily applied on a substrate. As the surfactant, conventional surfactants known in the art may be used without any particular limitation, and the addition amount may vary according to the kind of surfactant, the composition ratio of components of a mixture, the kind of solvent, and the kind of substrate.

Also, the resin composition of the present invention may include a stress reducing agent, a leveling agent, etc. as an additional additive.

An optical member according to the present invention includes the resin composition of the present invention.

Herein, when a film-type optical member is obtained by using the resin composition of the present invention, the resin solids including the compound represented by Formula 1 are usually included in an amount of 0.1 to 90 wt %, preferably of 1 to 50 wt %, and more preferably of 5 to 40 wt %, based on the total resin composition including a solvent. If the concentration of the resin composition is less than the lower limit, it is difficult to secure the thickness of a film, and if the concentration is greater than the upper limit, it is difficult to obtain a film having a uniform thickness due to high viscosity of a solution.

Also, the film obtained by using the resin composition of the present invention may be a uniaxially oriented film or a biaxially oriented film, and the polymer film may be used after surface treatment, such as hydrophilic treatment or hydrophobic treatment, and may be a laminated film or glass.

Also, the film may be made into a transparent film by using the resin composition of the present invention, and a melt-molding method or a solvent cast method, etc. In manufacturing the transparent film by the solvent cast method, the resin composition is applied on a support, such as a metal drum, a still belt, a polyester film, Teflon, etc., a solvent is dried in a drying furnace by using a roller, and then a film is peeled from the support. The amount of residual solvent in the transparent film is usually 10 wt % or less, preferably 5 wt % or less, and more preferably 1 wt % or less. If the amount of residual solvent is greater than the upper limit, the heat resistance of the film shows a tendency to be decreased. The manufactured transparent film may control the optical characteristic of the polymer resin by uniaxial orienting or biaxial orienting.

Reference will now be made in detail to the preferred embodiments of the present invention. However, the following examples are illustrative only, and the scope of the present invention is not limited thereto.

Example 1

1,4-Dibromobenzene was dissolved in an anhydrous THF solvent, and 1.0 equivalent of n-BuLi was gradually added at −78° C., followed by stirring at low temperatures for about 2 hours to generate anions. Then, 1.05 equivalents of a compound 1 was dropwise added thereto. After the completion of the addition, the temperature was gradually raised up to room temperature, followed by stirring at room temperature for about 2 hours. After the completion of the reaction, the mixture was worked up with hexane and water, and purified via silica gel to obtain a compound 2 at a yield of 95%.

The compound 2 was dissolved in an anhydrous THF solvent, and 1.05 equivalents of n-BuLi was gradually added at −78° C., followed by stirring at low temperatures for about 2 hours to generate anions. Then, excess CO₂ was bubbled, and after the completion of the reaction, 10% HCl was used to adjust pH to about 3. The mixture was worked up with ether and water, and purified via silica gel to obtain a compound 3 at a yield of 80%.

The compound 3 and 4-cyano-4′-hydroxybiphenyl were dissolved in CH₂Cl₂, and 1.1 equivalents of EDC and 0.1 equivalents of DMAP were added thereto, followed by stirring at room temperature for about 10 hours. After the completion of the reaction, the mixture was worked up with CH₂Cl₂, and recrystallized in hexane to obtain a final compound 4 at a yield of 85% or more. ¹HNMR of the compound 4 is as follows.

¹HNMR (400 MHz, CDCl₃): δ 0.30 (s, 6H), 0.69˜0.81 (m, 2H), 0.85˜0.93 (m, 3H), 1.20˜1.39 (m, 8H), 7.62 (d, 2H), 7.35 (d, 2H), 7.67 (d, 2H), 7.70 (d, 2H), 7.74 (d, 2H), 8.17 (d, 2H).

Example 2

1,4-Dibromobenzene was dissolved in an anhydrous THF solvent, and 1.0 equivalent of n-BuLi was gradually added at −78° C., followed by stirring at low temperatures for about 2 hours to generate anions. Then, 1.05 equivalents of a compound 5 was dropwise added thereto. After the completion of the addition, the temperature was gradually raised up to room temperature, followed by stirring at room temperature for about 2 hours. After the completion of the reaction, the mixture was worked up with hexane and water, and purified via silica gel to obtain a compound 6 at a yield of 92%.

The compound 6 was dissolved in benzene, and 0.1 equivalents of CuI, 0.03 equivalents of PdCl₂(PPh₃)₂, 5.0 equivalents of DBU, 0.5 equivalents of trimethylsilyl acetylene and 0.4 equivalents of H₂O were added, followed by stirring at 60° C. for about 10 hours. After the completion of the reaction, the mixture was worked up with 10% HCl and ether, and purified via silica gel to obtain a final compound 7 at a yield of 83%. ¹HNMR of the compound 7 is as follows.

¹HNMR (400 MHz, CDCl₃): δ 0.31 (s, 12H), 0.69˜0.80 (m, 4H), 0.86˜0.92 (m, 6H), 1.62˜1.71 (m, 4H), 7.45˜7.54 (m, 8H).

Example 3 Compatibility Test

90 parts by weight of general-purpose acrylate polymer resin (Mw=100,000), and 10 parts by weight of the compound synthesized in Example 1 were dissolved in 400 parts by weight of ethyl acetate (concentration=20 wt %), and the resultant solution was applied on glass and baked at 110° C. for 3 minutes. After storage of the resultant product at room temperature for 24 hours, whether solid was precipitated on the surface or not was observed by an optical microscope or naked eyes. FIG. 1 shows the result. According to the compatibility test result, an anisotropic compound was not precipitated, even after 24 hours.

Example 4 Compatibility Test

A compatibility test was carried out in the same manner as described in Example 3, except that the compound synthesized in Example 2, instead of the compound synthesized in Example 1, was used in an amount of 10 parts by weight. FIG. 2 shows the result. According to the compatibility test result, an anisotropic compound was not precipitated, even after 24 hours.

Comparative Example 1 Compatibility Test

1.0 equivalent of p-Hydroxybenzoic acid was dissolved in a mixed solvent (ethanol: water=7:3), and 1.0 equivalent of bromohexane and 2.2 equivalents of KOH were added, followed by stirring at 90° C. for about 10 hours. Then, ethanol was distilled under reduced pressure, and 10% HCl(aq) was gradually added to adjust pH to 1 to 3. Then, the resultant solid was subjected to filtration and drying, and the dried resultant product, together with 1.0 equivalent of 4-cyano-4′-hydroxybiphenyl, was dissolved in CH₂Cl₂. 1.1 equivalents of EDC and 0.1 equivalents of DMAP were added thereto, and stirring was carried out at room temperature for about 10 hours. After the completion of the reaction, the mixture was worked up with CH₂Cl₂, and purified via silica gel to obtain a final compound 8.

A compatibility test was carried out in the same manner as described in Example 3, except that the compound 8, instead of the compound synthesized in Example 1, was used in an amount of 10 parts by weight. FIG. 3 shows the result. According to the compatibility test result, after the manufacture of a film, precipitation of the compound 8 on the surface of the film was observed at room temperature.

Comparative Example 2 Compatibility Test

p-Iodophenol and Bromopropane (with the same equivalents) were dissolved in 1,4-dioxane, and was subjected to an alkylation reaction by K₂CO₃ base. Then, a compound 9 was prepared by a Pd coupling reaction of Example 2.

A compatibility test was carried out in the same manner as described in Example 3, except that the compound 9, instead of the compound synthesized in Example 1, was used in an amount of 10 parts by weight. FIG. 4 shows the result. According to the compatibility test result, after the manufacture of a film, precipitation of the compound 9 on the surface of the film was observed at room temperature.

Based on the results obtained from Examples 3 and 4, and Comparative Examples 1 and 2, it was determined that anisotropic silicon compounds represented by Formula 1 have high compatibility with a polymer resin. 

1. A silicon containing compound represented by Formula 1:

each of Q¹ to Q¹² independently represents —H, —F, —Cl, —Br, —I, —CN, —CF₃, —OCF₃, —R⁶, —OR⁶, —NHR⁶, —NR⁶R⁶ or —C(═O)R⁶; Z represents C or N, and herein, if Z is N, there is no bond with corresponding Q¹ to Q¹²; each of l, m and n independently represents an integer of 0 to 2, and l+m+n represents an integer equal to or greater than 1; each of Y, G¹ and G² independently represents —(CH₂)_(r)SiW¹W²(CH₂)_(s)—, —O—, —NR⁶—, —S—, —SO—, —SO₂—, —(CH₂)_(q)—, —CH═CH—, —C≡C—, —C(═O)O(CH₂)_(q)—, —OC(═O)(CH₂)_(q)—, —(CH₂)_(q)C(═O)O—, —(CH₂)_(q)OC(═O)—, —C(═O)(CH₂)_(q)—, —(CH₂)_(q)C(═O)—, —C(═O)NR⁶—, —NR⁶C(═O)—, —C(═O)S—, or —SC(═O)—, q represents an integer of 0 to 5, each of r and s independently represents an integer of 0 to 2; E represents —H, —F, —Cl, —Br, —I, —CN, —NCO, —NCS, —SiW¹W²R⁶, —R⁶, —N(R⁶)₂, —OR⁶, —CF₃, or —OCF₃; each of X¹ to X⁵ independently represents —SiW¹W²—, —O—, —NR⁶—, —S—, —SO—, —SO₂—, —(CH₂)_(p)—, —C(═O)NR⁶—, —NR⁶C(═O)—, —NR⁶C(═O)NR⁶—, —C(═O)O—, —OC(═O)—, or —OC(═O)O—, and p represents an integer of 0 to 2; W¹ represents —R⁷, —OR⁷, —NHR⁷, or —N(R⁷)₂; W² represents —R⁸, —OR⁸, —NHR⁸, or —N(R⁸)₂; each of R¹ to R⁸ independently represents —H, C₁˜C₂₀ alkyl, C₁˜C₂₀ fluoroalkyl, C₂˜C₂₀ alkenyl, C₂˜C₂₀ fluoroalkenyl, C₂˜C₂₀ alkynyl, C₂˜C₂₀ fluoroalkynyl, —(CH₂CH₂O)_(t)CH₃, —(CH₂CHCH₃O)_(t)CH₃, or —(CHCH₃CH₂O)_(t)CH₃, and t represents an integer of 1 to 5; and at least one of Y, G¹, G², E, and X¹ to X⁵ is a Si containing substituent, and herein, as the Si containing substituent, in Y, G¹ and G², —(CH₂)_(r)SiW¹W²(CH₂)_(s)— is introduced, in E, —SiW¹W²R⁶ is introduced, and in X¹ to X⁵, —SiW¹W²— is introduced.
 2. The compound as claimed in claim 1, wherein 1+m+n is an integer of 1 to
 3. 3. The compound as claimed in claim 1, wherein refractive anisotropy is 0.2 or more.
 4. The compound as claimed in claim 1, which is prepared by Reaction Scheme 1:

wherein ring A, ring B, ring C, ring D, l, m, n, G¹, G², and E are same as defined in claim 1, and each of L¹ and L² independently represents halide, mesylate, tosylate, or triflate.
 5. The compound as claimed in claim 1, which is prepared by Reaction Scheme 2:

wherein ring A, ring B, ring C, ring D, l, m, n, W¹, W², r, s, G¹, G² and E are same as defined in claim 1, and each of L¹ and L² independently represents halide, mesylate, tosylate, or triflate.
 6. The compound as claimed in claim 1, which is prepared by Reaction Scheme 3:

wherein ring A, ring B, ring C, ring D, l, m, n, G¹, G², R⁶ and E are same as defined in claim 1, and L¹ represents halide, mesylate, tosylate, or triflate.
 7. The compound as claimed in claim 1, which is prepared by Reaction Scheme 4:

wherein ring A, ring B, ring C, ring D, l, m, n, G¹, G² and E are same as defined in claim
 1. 8. The compound as claimed in claim 1, which is prepared by Reaction Scheme 5:

wherein ring A, ring B, ring C, ring D, l, m, n, q, G¹, G² and E are same as defined in claim 1, and each of L¹ and L² independently represents halide, mesylate, tosylate, or triflate.
 9. The compound as claimed in claim 1, which is prepared by Reaction Scheme 6:

wherein ring A, ring B, ring C, ring D, l, m, n, q, G¹, G², R⁶ and E are same as defined in claim 1, and L¹ represents halide, mesylate, tosylate, or triflate.
 10. The compound as claimed in claim 1, which is prepared by Reaction Scheme 7:

wherein ring A, ring B, ring C, ring D, l, m, n, q, G¹, G², R⁶ and E are same as defined in claim 1, L¹ represents halide, mesylate, tosylate, or triflate, and P represents a protection group.
 11. A resin composition comprising a polymer resin; and the silicon containing compound represented by Formula 1 as claimed in claim 1:

each of Q¹ to Q¹² independently represents —H, —F, —Cl, —Br, —I, —CN, —CF₃, —OCF₃, —R⁶, —OR⁶, —NHR⁶, —NR⁶R⁶ or —C(═O)R⁶; Z represents C or N, and herein, if Z is N, there is no bond with corresponding Q¹ to Q¹²; each of l, m and n independently represents an integer of 0 to 2, and l+m+n represents an integer equal to or greater than 1; each of Y, G¹ and G² independently represents —(CH₂)_(r)SiW¹W²(CH₂)_(s)—, —O—, —NR⁶—, —S—, —SO—, —SO₂—, —(CH₂)_(q)—, —CH═CH—, —C≡C—, —C(═O)O(CH₂)_(q)—, —OC(═O)(CH₂)_(q)—, —(CH₂)_(q)C(═O)O—, —(CH₂)_(q)OC(═O)—, —C(═O)(CH₂)_(q)—, —(CH₂)_(q)C(═O)—, —C(═O)NR⁶—, —NR⁶C(═O)—, —C(═O)S—, or —SC(═O)—, q represents an integer of 0 to 5, each of r and s independently represents an integer of 0 to 2; E represents —H, —F, —Cl, —Br, —I, —CN, —NCO, —NCS, —SiW¹ W²R⁶, —R⁶, —N(R⁶)₂, —OR⁶, —CF₃, or —OCF₃; each of X¹ to X⁵ independently represents —SiW¹W²—, —O—, —NR⁶—, —S—, —SO—, —SO₂—, —(CH₂)_(p)—, —C(═O)NR⁶—, —NR⁶C(═O)—, —NR⁶C(═O)NR⁶—, —C(═O)O—, —OC(═O)—, or —OC(═O)O—, and p represents an integer of 0 to 2; W¹ represents —R⁷, —OR⁷, —NHR⁷, or —N(R⁷)₂; W² represents —R⁸, —OR⁸, —NHR⁸, or —N(R⁸)₂; each of R¹ to R⁸ independently represents —H, C₁˜C₂₀ alkyl, C₁˜C₂₀ fluoroalkyl, C₂˜C₂₀ alkenyl, C₂˜C₂₀ fluoroalkenyl, C₂˜C₂₀ alkynyl, C₂˜C₂₀ fluoroalkynyl, —(CH₂CH₂O)_(t)CH₃, —(CH₂CHCH₃O)_(t)CH₃, or —(CHCH₃CH₂O)_(t)CH₃, and t represents an integer of 1 to 5; and at least one of Y, G¹, G², E, and X¹ to X⁵ is a Si containing substituent, and herein, as the Si containing substituent, in Y, G¹ and G², —(CH₂)_(r)SiW¹W²(CH₂)_(s)— is introduced, in E, —SiW¹W²R⁶ is introduced, and in X¹ to X⁵, —SiW¹W²— is introduced.
 12. The resin composition as claimed in claim 11, wherein weight ratio of the polymer resin: the compound represented by Formula 1 is 50:50 to 99:1.
 13. An optical member comprising the resin composition as claimed in claim
 11. 14. The resin composition as claimed in claim 11, wherein the compound is prepared by Reaction Scheme 1:

wherein ring A, ring B, ring C, ring D, l, m, n, G¹, G², and E are same as defined in claim 11, and each of L¹ and L² independently represents halide, mesylate, tosylate, or triflate.
 15. The resin composition as claimed in claim 11, wherein the compound is prepared by Reaction Scheme 2:

wherein ring A, ring B, ring C, ring D, l, m, n, W¹, W², r, s, G¹, G² and E are same as defined in claim 11, and each of L¹ and L² independently represents halide, mesylate, tosylate, or triflate.
 16. The resin composition as claimed in claim 11, wherein the compound is prepared by Reaction Scheme 3:

wherein ring A, ring B, ring C, ring D, l, m, n, G¹, G², R⁶ and E are same as defined in claim 11, and L¹ represents halide, mesylate, tosylate, or triflate.
 17. The resin composition as claimed in claim 11, wherein the compound is prepared by Reaction Scheme 4:

wherein ring A, ring B, ring C, ring D, l, m, n, G¹, G² and E are same as defined in claim
 11. 18. The resin composition as claimed in claim 11, wherein the compound is prepared by Reaction Scheme 5:

wherein ring A, ring B, ring C, ring D, l, m, n, q, G¹, G² and E are same as defined in claim 11, and each of L¹ and L² independently represents halide, mesylate, tosylate, or triflate.
 19. The resin composition as claimed in claim 11, wherein the compound is prepared by Reaction Scheme 6:

wherein ring A, ring B, ring C, ring D, l, m, n, q, G¹, G², R⁶ and E are same as defined in claim 11, and L¹ represents halide, mesylate, tosylate, or triflate.
 20. The resin composition as claimed in claim 11, wherein the compound is prepared by Reaction Scheme 7:

wherein ring A, ring B, ring C, ring D, l, m, n, q, G¹, G², R⁶ and E are same as defined in claim 11, L¹ represents halide, mesylate, tosylate, or triflate, and P represents a protection group. 